The effect of surface modification for nano calcium carbonate to coating

 The effect of surface modification for nano calcium carbonate to coating

The surface modification of nano-calcium carbonate was carried out, and the modified calcium carbonate was characterized and filled in the coating to investigate the performance of the coating. After modification, the organic film on the surface of calcium carbonate is oleophilic, and the surface can not be easily aggregated and filled in the coating. Its flexibility, hardness, leveling and gloss are better than those of the unmodified nano calcium carbonate.
Nano CaCO3 is a new type of high-grade functional filling material with dimension size in the order of nanometer (1-100nm). It has wide application prospect in many fields such as rubber, plastic, ink, coating and papermaking. Compared with the ordinary micron CaCO3, nano-CaCO3 is directly applied to the organic medium, there are two shortcomings: First, the surface of the particles can be high, thermodynamically unstable, easily gathered into groups, thus affecting the practical application of nanoparticles Effect; second: CaCO3 surface hydrophilic oleophobic, was strong polarity, in the organic medium is difficult to evenly dispersed, and there is no binding between the base material, easy to cause interface defects, resulting in decreased material properties.
Therefore, it is necessary to surface modification of nano-CaCO3 in order to eliminate the surface high energy potential, adjust the hydrophobicity, improve the wettability and adhesion between the organic base material, so as to maximize the material performance and filling capacity, cost.
Polyurethane varnish performance test results show that modified nano-calcium carbonate filled varnish, its flexibility, hardness, leveling, gloss are better than unmodified calcium carbonate filled varnish. This is due to the formation of a tough film between the particle and the binder interface due to the adsorption modifier on the surface of the modified nano-calcium carbonate, which can be moderately stressed at the interface between the high modulus calcium carbonate and the low modulus organic binder Transfer, improve the flexibility and hardness of the coating, and because the modified nano-calcium carbonate dispersed in the coating matrix, and unmodified nano-calcium carbonate because the surface energy is high, in the state of aggregation, so the modified calcium carbonate filled Paint luster, leveling, flexibility, hardness is better than unmodified.